Sandvik Bioline cored wire (Wire)
Datasheet updated 2013-02-18 14:23:37 (supersedes all previous editions)
Sandvik Bioline cored wire (SBCW) is a composite wire consisting of a Sandvik Bioline F562 CoCrMo alloy shell and a secondary alloy as the core material. The core material is typically pure silver (Ag) to promote increased conductivity relative to solid Sandvik Bioline F562. However, other core materials such as platinum (Pt), gold (Au) and tantalum (Ta) can be selected in order to increase the radiopacity or provide other unique combinations of properties to the composite wire. The standard core dimension is 25% by area, however other core sizes can be considered.
The outer component is characterized by:
- Excellent corrosion resistance
- Excellent fatigue properties
- High strength combined with good ductility
The inner silver core provides:
- High electrical efficiency
- Electrical conductivity
- Low electrical resistance.
Sandvik Bioline cored wire can be used for cochlear implants, pacemaker, defibrillator leads and varicose vein surgery devices.
Sandvik Bioline F562 grade is according to the following standards:
Chemical composition (nominal) %
NB :The chemical composition in the table applies to the shell material only.
Purity of core material to be specified by customer (Ag purity typically > 99.99%)
The mechanical properties of Sandvik Bioline cored wire (SBCW) will depend on the chemical composition of the core material, the cross sectional area of the core material and the temper (annealed, cold worked or cold worked and aged).
Standard tensile strength values in MPa for silver filled Sandvik Bioline F562 as a function of cold worked and % cross sectional area (CSA) silver are given in the following table.
Note : A cold work percentage greater than 65% is not recommended for this material.
|Tensile Strength Rm MPa|
|Silver CSA||0 % CW||20 % CW||30 % CW||40 % CW||50 % CW||60 % CW|
The electrical resistance of Sandvik Bioline cored wire depends on the selection of core alloy, cross sectional area of the core, temper and final size.
The nominal electrical resistance of 0.100 mm silver filled cored wire in the annealed and cold worked condition is given in the following table.
|% silver (Ag)||25||30||35||40||45|
The table below shows electrical resistivity (unit : ohm/m) of solid F562 versus Sandvik Bioline cored wire at different common sizes as a function of silver content:
|% silver (Ag)*||Diameter, mm|
|0 - solid Sandvik Bioline F562||2037.0||127.3||81.5||56.6||41.6||20.4|
* 25 % silver means 25% Ag filled Sandvik Bioline F562 version
Forms of supply
The wire can be supplied in annealed, cold worked or cold worked and aged condition.
The wire can also be provided in a square or rectangular profile.
A smooth diamond drawn finish is provided at all size ranges and round wire or ribbon can be coated with an advanced polymer coating.
SBCW is typically supplied on plastic spool but other packaging methods are also available.
Sandvik Bioline Cored Wire (SBCW) is available in sizes ranging from 0.025 mm to 3 mm. Smaller and larger diameters can be supplied on request.
The standard outside diameter tolerances for SBCW are given as a function of size range in the following list. Special tolerances are available on request.
|OD range, mm||Tolerance, mm|
Sandvik Bioline Cored Wire (SBCW) is a preferred grade of composite wire for medical applications because the highly favorable combination of excellent corrosion resistance, high strength and moderate conductivity.
Typical applications are lead wires for medical devices such as pacemakers, defibrillators and cochlear implants.
Disclaimer: Sandvik is not providing any products or services that are intended or may be construed to be recommending or otherwise advising on, in any manner, the design, suitability, appropriateness or effectiveness, from a medical/biological/safety perspective, of any medical material, instrument and/or medical device.