Sandvik 430 (Plate and sheet)
Datasheet updated 2012-08-03 09:36:07 (supersedes all previous editions)
Sandvik 430 is a ferritic stainless steel with minimum 16% chromium. Due to its ferritic structure Sandvik 430 has a lower tensile strength, elongation and impact resistance than the austentic stainless steels. The proof strength is somewhat higher.
Standards
- ASTM 430
- UNS S43000
- W.Nr. 1.4016
Product standards
ASTM A240, A480
Chemical composition (nominal) %
| C | Si | Mn | P | S | Cr | Ni |
|---|---|---|---|---|---|---|
| 0.12 | 1.0 | 1.0 | 0.040 | 0.03 | 16-18 | 0.75 |
Forms of supply-finishes and dimensions
Sheet and coil
Sheet and coil may be supplied as annealed and pickled, polished or in the bright-annealed condition
The size ranges available ex-mill are given below.
Thickness Range Max Width Finishes
0.7 - 1.50 mm 1219mm 2D, 2B & No4
2.0 - 3.00 mm 1500mm 2D & 2B
Mechanical properties
At 20°C (68°F)
| Proof strength | Tensile Strength | Elong. | ||
|---|---|---|---|---|
| Rp0.2a) | Rm | Ab) | ||
| MPa | ksi | MPa | ksi | % |
| min | min | min | ||
| 205 | 30 | 450 | 65 | 22 |
1 MPa = 1 N/mm2
The hardness (Brinell) is approximately 183, (Rockwell B) 89
Physical properties
Density 7.79 g/cm3
Thermal conductivity at 20 oC 25 W/mK
Modulus of Elasticity 220 GPa
Magnetisability Yes
Specific Heat at 20 oC 460 J/kgK
Thernal Expansion between
- 20 & 200 OC 10.0 x 10-6
- 20 & 400 OC 10.5 x 10-6
Disclaimer: Recommendations are for guidance only, and the suitability of a material for a specific application can be confirmed only when we know the actual service conditions. Continuous development may necessitate changes in technical data without notice. This datasheet is only valid for Sandvik materials.
Send PDF via email
Article functions
Related information
Print this datasheet
Export to PDF
Download this datasheet as PDF or send by email.
Download as PDF
Send PDF via email